How to select the diamond cutting tools, PCD cutting tools and CBN cutting tools for the products to be processed

Many people are confused how to select the corresponding cutting tools for the products to be processed! Now it is to illustrate the advantages of the diamond cutting tools, PCD cutting tools and CBN cutting tools for everyone.
Advantages of PCD cutting tools:
To process the aluminum workpieces, the PCD cutting tools are characterized with long service life, high metal removal rate and other advantages; however, the PCD cutting tools are expensive and have a high processing cost. The aluminum material performance at present cannot be rivaled that in the past; when processing a variety of newly developed aluminum alloy materials, to achieve the optimization of the productivity and machining quality, it is necessary to carefully choose the grade number and geometric parameters of the PCD cutting tools so as to adapt to different processing requirements. The another change of the PCD cutting tools falls on the constantly decreased processing cost; under the joint actions of the market competition pressure and the improved cutting tool manufacturing process, the price of the PCD cutting tools has been substantially reduced more than 50%. The above-mentioned change trend has led to the increasing application of the PCD cutting tools in the aluminum material processing while the applicability of the cutting tool is restrained by different materials to be processed.
Advantages of CBN cutting tools:
They can greatly reduce the cutter change times and cutting tool wear, compensate the time spent in adjusting the machine so as to give full play to the high efficiency of the numerically-controlled machine tool, which will further allow the turning processing (using turning instead of grinding) after the quenching on one numerically-controlled machine tool; meanwhile, they allow to be used for repeated grinding.
Advantages of Diamond cutting tools:
Hardness－60000100000MPa, determined by the direction and temperature of the crystal
Bending strength－210490MPa
Compressive strength－15002500MPa
Elasticity modulus－910.510123MPa
Heat conductivity－8.416.7J/cms℃
Massic heat capacity－0.156J/g℃) room temperature)
Oxidation onset temperature－9001000K
Graphitization onset temperature－in 1800K inert gas)
Coefficient of friction between aluminum alloy and yellow copper-0.050.07 under room temperature)